Originally Posted by John long
Brian, when I made my post I was not disagreeing either. I meant low heat into the panel, not a low heat weld. Short and fast is correct and that takes enough heat for fast penetration. Sorry if I did not make my self clear.
No problem John, don't ever worry about that, we are tossing stuff out there. If there aren't different ideas being tossed into the mix how in the hell can we learn?
If I wanted to get ONE point of view, I'd read a book. We are here to DISUSS things and see many different ways to get the job done.
And to learn there are better ways than we are doing it too. I personally WANT to be shown better ways that the way I do things, if it makes sense it makes sense, you can't disagree when it makes sense.