Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic -- Hot Rod Forum

Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Garage - Tools> Heat Treating Soft Metal (Tools)
User Name
lost password?   |   register now

Thread: Heat Treating Soft Metal (Tools) Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:
Please select your insurance company (Optional)


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

Additional Options
Miscellaneous Options

Topic Review (Newest First)
04-19-2011 04:27 PM
scrot The Cherry Red looks interesting, and not that expensive.
04-19-2011 09:13 AM
Originally Posted by evolvo
You got me thinking so I googled it

lots to learn!

That suggests tempering at 325 deg, not likely to accomplish much at that low of a temperature and for a "one size fits all" tempering temperature 400 deg to 425 deg in an oven for a hour would be better. If the type of steel is not known, or close to it, then using ball-park figures for the heat to either harden or temper is going to a hit-or-miss proposition at best.
04-19-2011 09:07 AM
oldred They are almost certainly mild steel and as such can not be hardened/tempered. Probably something like one of the very common 1018 or 1026 steels and heat treating them would be a waste of time. You could use some "Kasenit" or "Cherry red" hardening compounds to case harden them which would harden them to a few thousandths deep but leave the inside soft and less likely to break. Simply heating them red hot and plunging in oil or water will harden tool steels and other alloy steels but then they are brittle and very easy to break. Hardening must be followed by tempering at a lower temperature for a specified period to achieve toughness without losing the hardness. Hardening is a two step process and the tempering step can not be skipped. All this however unfortunately does not work, as already mentioned, for mild steels and that is almost certainly what those screwdrivers are.
04-18-2011 10:31 PM
evolvo You got me thinking so I googled it

lots to learn!
04-18-2011 09:23 PM
JohnnyK81 Won't hurt to try! Temper it after though.
04-18-2011 08:51 PM
Heat Treating Soft Metal (Tools)

I have some cheap Harbor Freight screwdrivers and other tools that I know are made out of soft metal that I'd like to harden.

Can the tips of the screwdrivers be heat treated to harden them?

They are essentially useless since they are so soft.

If the tips are heated red hot and dipped in oil will that make them better or just "screw" them up?

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

All times are GMT -6. The time now is 08:30 PM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
vBulletin Security provided by vBSecurity v2.2.2 (Pro) - vBulletin Mods & Addons Copyright © 2017 DragonByte Technologies Ltd.
Copyright 1999 - 2012. All Rights Reserved.