Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic
Hotrodders.com -- Hot Rod Forum



Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Hotrodding Basics> stock 400 crank cast or cast steel?
User Name
Password
lost password?   |   register now

Thread: stock 400 crank cast or cast steel? Reply to Thread
Title:
  
Message:
Trackback:
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Password
Please enter a password for your user account. Note that passwords are case-sensitive.
Password:
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:

Log-in

Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.



Additional Options
Miscellaneous Options

Topic Review (Newest First)
12-27-2011 06:21 PM
oldbogie
Quote:
Originally Posted by 67-4-fun
are the stock 400 sbc crankshafts a full cast or cast/steel? I think they are full cast but i wanted to ask just to be sure. also what are there rpm limits?
Calling this steel is something of a stretch, it is ASTM A536 spec nodular iron.
That said they will take some pretty good abuse. This spec covers stuff with tensile strength limits for about 60 to 100,000 pounds/in^2 depending on the spec. There are those who think the 9000 cast steel shaft is 80-60-06 grade, that I can't confirm.The 80 is the minimum tensile tensile strength in the grade, that's not to say the alloy can't exceed that Not up to the typical GM 1053 forging where the material is rated at 110,000. The middle number is the minimum yield strength which would be where it deforms. The 06 spot is the elongation, small numbers here mean a brittle material , big numbers a less brittle material. What this tells you is that the casting will stretch very little before it hits its ultimate strength and breaks. Where a large number like 22% in the case of the 1053 forging tells you it will stretch quite a ways before it lets go. Years ago Pontiac and Buick actually used this nodular cast stuff quite successfully for connecting rods, they called it Arma Steel, but it was nodular iron just the same.

All of these numbers are theory of course, the design, manufacturing process with its variability, and environmental exposure one to the next can greatly influence just how deep into these theoretical numbers you can push any particular part.

A good balance job and a good damper does a lot to stretch the load limits with a cast crank. Typically about 500 horses and 6000 RPM is about the upper limit, you can trade horses for RPM, say 400 at 7000 would be a reasonable max. The other element is gear changing and wheel spinning starts. With a stick gear box the shock loads on the crank are pretty high so the power needs to back off 50 or the revs 500.

Bogie
12-27-2011 05:49 PM
67-4-fun ok, well i was told around 6500rpm with a well balance assembly but just wanted to get another opinion or a clarification just to be sure
12-27-2011 01:15 PM
BOBCRMAN@aol.com Good old wonder metal... Cast iron.. Rpm capability depends on many things.. Rotating/reciprocating assembly weight/balance being one.
12-27-2011 12:07 PM
67-4-fun
stock 400 crank cast or cast steel?

are the stock 400 sbc crankshafts a full cast or cast/steel? I think they are full cast but i wanted to ask just to be sure. also what are there rpm limits?

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off


All times are GMT -6. The time now is 11:14 AM.


Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2014, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
Copyright Hotrodders.com 1999 - 2012. All Rights Reserved.