i talked to the guys at airgas about the 84/16 steelmix
they said it would make my life easier on the thin stuff
(compared to the 75/25 that I had been using )
so thats what I got
did I screw up? anyone else use it?
I remember it was mentioned by someone in a thread a while back
You probably didn't get hurt as long as they didn't charge much extra for it but I doubt it will help with the thin stuff very much. There are all kinds of gas mixes out there, some even have more than two. These tri mixes can even have small amounts of Oxygen which seems to be a contradiction but in certain conditions it can help, usually these exotic gases are for industrial use and the main concerns are speed/production costs more than anything else. Most of them will work just fine for the type of welding you are doing however and unless they charged you a big premium it should not matter much one way or the other. Actually depending on your welder, the wire you're using and surface condition you may very well see a slight improvement, or not, but I wouldn't expect it to be anything to get excited over.
75/25 has been the standard mix for many years and every ratio possible has been tried but the old standard C25 has always been the best for all-around use for a good reason,
i am not expecting miracles, but while im welding these patch panels etc.
i am thinking every little bit would help, me and the thin stuff dont see eye2eye:mwink:
This is an older thread, you may not receive a response, and could be reviving an old thread. Please consider creating a new thread.
Related Threads
?
?
?
?
?
Hot Rod Forum
2.2M posts
175.7K members
Since 2001
A forum community dedicated to hot rod owners and enthusiasts. Come join the discussion about restoration, builds, performance, modifications, classifieds, troubleshooting, maintenance, and more!