Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic
Hotrodders.com -- Hot Rod Forum



Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Body - Exterior> Metal Prep / Conditioner vs. Self Etching Primer
User Name
Password
lost password?   |   register now

Thread: Metal Prep / Conditioner vs. Self Etching Primer Reply to Thread
Title:
  
Message:
Trackback:
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
If you do not want to register, fill this field only and the name will be used as user name for your post.
Password
Please enter a password for your user account. Note that passwords are case-sensitive.
Password:
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:

Log-in

Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.



Additional Options
Miscellaneous Options

Topic Review (Newest First)
05-15-2013 05:36 AM
deadbodyman X-2 ,metal prep to epoxy,,,,also back when I did use etch primer (duponts variprime) filler didnt stick to it very well...
05-13-2013 10:04 AM
BarryK
Quote:
Originally Posted by tech69 View Post
metal prep to epoxy is better than a self etching primer in my opinion.


Exactly!
Both PPG and Dupont have an excellent metal prep process, if you follow their instructions to a tee, if not good luck.
05-12-2013 04:16 PM
Pats55 30 years using Metal Prep never a problem either
05-12-2013 07:24 AM
Old Fool I stopped using metal prep a few years ago when I discovered SPI epoxy. Now I just sand with 80g or blast the rust away, clean with w&g remover and shoot 2 coats of SPI epoxy directly to the metal whether it is alum or steel .
Less products to buy, less products to misuse, and results are awesome.
05-11-2013 07:50 PM
Chevymon Normally steel and aluminum would require two different types of conditioner.
05-11-2013 02:56 PM
TucsonJay I've been using metal prep (phosphoric acid) since the early seventies with zero issues. It simply changes iron oxide (rust) to iron phosphate... which is a dead gray material that is not in an "ongoing process", like rust is. It also acts as a mild degreaser.

If you pay attention, you can actually watch the rust turn from orange to gray. If a spot is tubborn, just scotchbrite it and wet-and-wipe again with prep.

I like R-Ms 801 prep, which contains alcohol, and does not require rinsing. Just wet it good... let it sit for a moment... and wipe it away. 30-60 minutes later you can paint. ....and you aren't spending unnecessary dollars on primer and labor.

Not everything being sold is necessarily a better idea. Metal prep has been working for around a hundred years.
05-11-2013 08:39 AM
tech69 metal prep to epoxy is better than a self etching primer in my opinion.
05-11-2013 07:58 AM
eisej
Metal Prep / Conditioner vs. Self Etching Primer

I have a bike tank that I am painting and on it's edges I have some chips down to metal. Otherwise the factory paint is mint. Of course my first thought was that I have to use a self etching primer which bent me because I had to buy more. Then I remembered I had some metal prep/conditioner that I was using to keep some aluminum from corroding after some restoration work I was doing.


My question is, bike tank paint aside, if I have a bare piece of mild steel whether it be a fender or anything else, is it ok, not ok, or "at my own risk" to use the metal conditioner/prep which is basically a very mild type of acid (what type I'm not sure. Maybe phosphate?) and then a primer/sealer or primer filler, instead of using a self etching primer on said bare metal? Of course all other preparations before paint being completed.

Thanks for the knowledge transfer.

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off


All times are GMT -6. The time now is 05:37 AM.


Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2014, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
Copyright Hotrodders.com 1999 - 2012. All Rights Reserved.