Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Body - Exterior> Welding stress fracture in sheet metal
User Name
lost password?   |   register now

Thread: Welding stress fracture in sheet metal Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:
Please select your insurance company (Optional)


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

Additional Options
Miscellaneous Options

Topic Review (Newest First)
07-31-2005 08:45 AM
theHIGHLANDER The only problem with MIG is using the wrong wire for the job. I would weld that with .023 with an ER70S2 or 3 wire. Not always available since most welding is structural and most suppliers only stock 'S6 or 7. The S2 is made for doing sheetmetal. It grinds easy and has less shear strength than the others. Perfect for body panels. Zap it in 1 spot at a time overlapped so it looks like a tig weld and forget it for life. It works for me.
07-31-2005 08:00 AM
baddbob I guess I need math help,
07-31-2005 07:28 AM
UKLuge66 Thanks everyone. I thought oxyacetylene may be a better choice here, but I was not sure. The crack is small and it is not structurally critical but I want to repair it for cosmetic reasons, even though you can only see it with the hood open.

The car was built in October 1965; registered as a '66 when it was first sold. It is an MG Midget. Not exactly a hotrod, but you know those yappy little mutts that think they're big dogs? Same thing here.
07-30-2005 07:39 PM
baddbob A small 3/4" crack shouldn't be anything to get all concerned about IMO, I'd gas weld it without hesitation, or a mig should work fine-just put a good weld down that's hot enough so it isn't brittle, don't over grind the weld causing the basemetal to thin and it should be fine. Or you could section 1/4" out of the cracked area and make a filler out of 1/4" round stock welded in place then grind to shape. I agree a small backing properly brazed in place would add a lot of strength and would be more crack resistant than just welding the crack. 40 year old fender, is this car a 55?
07-30-2005 11:13 AM
shine it's woth getting tig welded. cracks are a tuff fix at best.
07-30-2005 09:57 AM A highly stressed area like that is not a good place to MIG since the MIG bead is so hard and relatively brittle. Brazing is a poor substitute, again because it is weaker than the surrounding metal and will eventually break in exactly the same place. You see a lot of old fenders with cracks that were repaired like that and are re-broken. IMHO, oxy/acetylene is the only proper fix of those fender edge tears. No need to pre-drill the crack root. Use a clamp to hold the edges together and run your welding bead right down the center of the crack using standard 1/16" mild steel filler rod. A little grinding and the fix is as strong as the base metal. Although gas welding dumps a lot of heat into the metal compared to MIG or better yet TIG, edges of fenders are almost always in a highly compound curved area which are much more resistant to heat damage than flat body panels. There may be a slight shrinkage dip next to the weld that you can easily tap out but there won't be that dreaded full panel warpage.
07-30-2005 09:42 AM
Welding stress fracture in sheet metal

I have a 40 year old fender that has a small stress crack (3/4" long) on the lip that forms the inner edge for the hood opening. The crack is located where the fender is supported by the grill surround.

I would normally open up the crack and weld or braze a small piece of metal behind it to form a doubler to give added support to that area. But, due to its location I cannot increase the thickness of the metal.

What are my options for repair? First I thought that I should drill a small hole where the crack ends to keep it from traveling further.

I could MIG weld the crack, but I fear the concentrated heat will embrittle the metal next to the weld causing it to crack next to the repair.

I could Oxyacetylene weld the crack, thinking that the additional heat may anneal the area if cooled slowly thereby making the repair less likely to crack, but not sure.

I don't think I should braze the crack since the metal does not overlap; I am afraid the repair would not hold up.

Any thoughts? Thanks for your help!

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

All times are GMT -6. The time now is 02:48 PM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
vBulletin Security provided by vBSecurity v2.2.2 (Pro) - vBulletin Mods & Addons Copyright © 2017 DragonByte Technologies Ltd.
Copyright 1999 - 2012. All Rights Reserved.