Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic -- Hot Rod Forum

Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Body - Exterior> Soda blasted projects-is it too late to save?
User Name
lost password?   |   register now

Thread: Soda blasted projects-is it too late to save? Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:
Please select your insurance company (Optional)


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

Additional Options
Miscellaneous Options

Topic Review (Newest First)
05-09-2011 06:06 PM
hrjme As I said, the soda blasting was done by a professional aircraft painter, who does corporate air craft as a profession. Since he was one of the few people I could find at the time that did soda blasting regularly, and figuring he know how to avoid distortion on large soft panels, I believe he was a good choice. I did have concerns about cleanup, and we discussed it. I told him to prep and primer so as to make sure it was done properly, aqs if it was his own restoration.

As an aside, He chose to use a mixture of soda and garnet on the rusty areas. He claimed garnet was better than sand or glass on steel, to avoid painting problems.

As to my little current project, I will take the advice for multiple washes, etc before the primer coat.
05-09-2011 05:30 AM
jeremyb you need to wash the radiator good with dawn soap and water, or simple green and water. then degrease, epoxy, and paint. refer to the tech sheets for propper application...

as for the car body, if it wasn't washed to neutralize the soda, before the epoxy was applied, you need to strip it and start over. doesn't matter how long it has sat with epoxy on it. if not, after paint, once it gets in the sun good tiny bubbles will start to appear in various places over the car. those could lead to bigger bubbles. even just a few hours in the sun can cause it to start bubbling. even worse, you start to lose adhesion of the epoxy to the metal.

something you probably dont want to hear, but its the truth.
05-08-2011 06:34 PM
OneMoreTime Main thing is with soda is that the parts need to be throughly water and soap and then blow off the moisture..See soda is an alkali and reacts with the acid etch in a lot of primers which interferes with adhesion..If the parts were well cleaned you may be ok..

05-08-2011 06:13 PM
Soda blasted projects-is it too late to save?


After reading the above posts about soda blasting, I find I may have problems. First, several years ago, I had our 41 sedan body blasted by a professional aircraft re-finisher. Most of his work is on aluminum airplanes, but he also does autos. I had him soda blast and epoxy prime the body and parts, knowing that restoration work will take years. This is a complete frame off restoration. It is still under construction, but is nearing beginning the paint processes.

The second concern is a rebuilt radiator for a 23 T-bucket. I hooked up a used 40 pound pressure blaster with an Eastwood soda blasting valve kit. I soda blasted all exterior metal, except the repainted new core. The radiator frame and tank are mostly exposed, so will need painting to match the glass shell and car body. Most is copper, brass and soldered seams. I will be doing the radiator painting myself, using DuPont's Urethane single stage paint and epoxy primer.

So, from the tone of the posts in the above thread, I am in trouble with both projects. Any advice, especially on the brass works?

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

All times are GMT -6. The time now is 04:48 AM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
vBulletin Security provided by vBSecurity v2.2.2 (Pro) - vBulletin Mods & Addons Copyright © 2017 DragonByte Technologies Ltd.
Copyright 1999 - 2012. All Rights Reserved.