Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic -- Hot Rod Forum

Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Suspension - Brakes - Steering> 110 ARC vs 110 MIG
User Name
lost password?   |   register now

Thread: 110 ARC vs 110 MIG Reply to Thread
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Please enter a password for your user account. Note that passwords are case-sensitive.
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:
Please select your insurance company (Optional)


Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.

Additional Options
Miscellaneous Options

Topic Review (Newest First)
08-28-2003 03:49 PM
Cowtown Punk Well, I already have a 110 MIG and I am almost finished with the chop on my car and it is almost time to put in the front cross member. Some say I can use it some say I can't. When you flip the lid on my Lincoln 135 it says that I can use flux core and weld thicker material then what my frame is made of. The motor I built is going to have huge amounts of torque. I would hate to take someone for a ride in my car a crash. The frame is a 41 ford.
08-28-2003 06:58 AM
farna A 110V MIG should be good. You can weld 3/16" - 1/8" thick material from one side in one pass depending on the welder you buy. If you can get to both sides of an item, you can weld almost twice the thickness stated. MIG welders are easier to learn to use and distort metal less.

What you call an "ARC" welder is really a "shielded metal arc welder" (SMAW), commonly called a "stick" welder. MIG, TIG, and SMAW and all forms of electric arc welding. The SMAW is great for heavy material, 1/8" and thicker. It's difficult (but not impossible) to weld thinner material. For thick metal you "drag" the torch, with the wire angled toward the weld that you just laid and as close to 90* over the joint as possible. Lean the torch 15-20* in the direction of travel. For thin material you "push" the torch in FRONT of the weld, angled 15-20* AWAY from the direction of travel. This lets the weld cool more and distorts the metal less. THE ANGLES ARE CRITICAL, especially the 90* over the work. It's hard to describe without pics, but if the angles aren't right, there will be to little or to much penetration.

With the MIG, if the material is over 1/8" or you can't get to both sides, just bevel the edges then weld. Leave a 3/16" flat where the two pieces come together, bevel above this. Leave a gap the thickness of the welding wire between the 3/16" flats to insure proper penetration.

Pick up the book that Home Depot and Lowe's sells on welding and read through it before you buy. That will give you a better idea of what you need and how to do it. After that it's just practice.

Oh yeah, I'm a basic welding instructor for the USAF.
08-28-2003 04:20 AM
zonk Feel both are just as good,I prefer the mig ,one that can use gas,or flux core wire.the mig feel is alot more useful
08-27-2003 10:51 PM
Cowtown Punk Ok, so I get a bigger welder, say the ARC and the MIG are the same which would be better for frame work?
08-26-2003 08:08 PM
unstable 110 mig will handle 1/8 inch thick using flux core in one pass...
I'd imagine if you were skilled, you could weld thicker using several passes...but if you question your skill level, cross members aren't something I'd partake in.
08-26-2003 07:15 PM
zonk I question either one would be big enough to do any frame welding to have good penetration to be safe,my opinion at least 175 amps to safely weld what you're wanting to do.
08-26-2003 06:59 PM
Cowtown Punk
110 ARC vs 110 MIG

Which welder is better for installing cross members on a frame? 110 Arc or 110MIG using Flux core????

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

All times are GMT -6. The time now is 03:03 PM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
vBulletin Security provided by vBSecurity v2.2.2 (Pro) - vBulletin Mods & Addons Copyright © 2017 DragonByte Technologies Ltd.
Copyright 1999 - 2012. All Rights Reserved.