Hot Rod Forum : Hotrodders Bulletin Board - Reply to Topic
Hotrodders.com -- Hot Rod Forum



Register FAQ Search Today's Posts Unanswered Posts Auto Escrow Insurance Auto Loans
Hot Rod Forum : Hotrodders Bulletin Board > Tech Help> Body - Exterior> Anyone use heat to thin lacquer or urethanes?
User Name
Password
lost password?   |   register now

Thread: Anyone use heat to thin lacquer or urethanes? Reply to Thread
Title:
  
Message:
Trackback:
Send Trackbacks to (Separate multiple URLs with spaces) :

Register Now

In order to be able to post messages on the Hot Rod Forum : Hotrodders Bulletin Board forums, you must first register.
Please enter your desired user name (usually not your first and last name), your email address and other required details in the form below.
User Name:
Password
Please enter a password for your user account. Note that passwords are case-sensitive.
Password:
Confirm Password:
Email Address
Please enter a valid email address for yourself.
Email Address:

Log-in

Human Verification

In order to verify that you are a human and not a spam bot, please enter the answer into the following box below based on the instructions contained in the graphic.



Additional Options
Miscellaneous Options

Topic Review (Newest First)
02-12-2012 05:03 PM
rsfyj
Always used a Hot Plate

We always heated the old transport Enamel it went on nicer and the early enamel with hardners.good old days
02-12-2012 07:31 AM
gow589 I had a can of chassis black on a paint roller. It was a little too cool to paint. I put a space heater on it for short bit to bring it up to temp.

I ran a quick errand into town and forgot about it. I got home to a black wall of paint.
02-12-2012 05:53 AM
Old Fool heat trace cable is intended to be used with a thermostat that shuts of at a relatively low temp. it is to stop freezing, never intended for being used as a hot pad which would have been a much more intelligent choice.
02-11-2012 11:42 AM
777funk I ended up using a heat trace cable (recommended by a specialty shop that sells rigs like what I'm describing) and wrapped it in foil and in pipe insulation around my pressure pot's fluid hose.

It actually did the thinning I was after. My temps were around 140F and very steady. Worked very good to thin the material, it atomized beautifully. However I was still having to spray too much material to get it to flow out and solvent pop was the result (lots of tiny trapped air bubbles).

So back to thinning my lacquer 50/50.

The kicker for me was when the heat trace arced. Not a pleasant sound next to a pot full of lacquer and sprayed mist in the air. That's the end of heating for me (at least with my current setup). I really wouldn't have expected the specially designed heat trace cable to malfunction in use. But I guess if it can go wrong it will.
09-26-2011 08:44 AM
31Vicky In line heaters have been and are used on production lines to eliminate the need for additional solvents. If you can control the heat, I would never heat them more the 120 to 140 F.
09-25-2011 02:35 AM
am88lude it doeswork just use one of those electric hot plate thigns. i'd be carefull though they tend to be flammable
09-25-2011 02:25 AM
milo I use those coffee cup warmers or candle warmers to bring temps up on all materials

http://youtu.be/tisgnyHkzSk
09-24-2011 10:57 PM
777funk
Anyone use heat to thin lacquer or urethanes?

I've heard that heating lacquer to a high temp can help thin the material instead of using lacquer reducers. Anyone ever done this?

Posting Rules
You may post new threads
You may post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off


All times are GMT -6. The time now is 07:21 PM.


Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2014, vBulletin Solutions, Inc.
Search Engine Optimization by vBSEO 3.6.0 PL2
Copyright Hotrodders.com 1999 - 2012. All Rights Reserved.